EN 1.4401 Stainless Steel vs. EN 1.4567 Stainless Steel

Both EN 1.4401 stainless steel and EN 1.4567 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4401 stainless steel and the bottom bar is EN 1.4567 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
190 to 240
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 40
22 to 51
Fatigue Strength, MPa 200 to 320
190 to 260
Impact Strength: V-Notched Charpy, J 91 to 94
91 to 110
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
76
Shear Strength, MPa 410 to 550
390 to 490
Tensile Strength: Ultimate (UTS), MPa 600 to 900
550 to 780
Tensile Strength: Yield (Proof), MPa 230 to 570
200 to 390

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 950
930
Melting Completion (Liquidus), °C 1440
1410
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
11
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 19
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.8
3.1
Embodied Energy, MJ/kg 52
43
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 26
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
150 to 220
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 800
100 to 400
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
19 to 27
Strength to Weight: Bending, points 20 to 26
19 to 24
Thermal Diffusivity, mm2/s 4.0
3.0
Thermal Shock Resistance, points 13 to 20
12 to 17

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.040
Chromium (Cr), % 16.5 to 18.5
17 to 19
Copper (Cu), % 0
3.0 to 4.0
Iron (Fe), % 62.8 to 71.5
63.3 to 71.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 10 to 13
8.5 to 10.5
Nitrogen (N), % 0 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015

Comparable Variants