EN 1.4401 Stainless Steel vs. SAE-AISI 1008 Steel

Both EN 1.4401 stainless steel and SAE-AISI 1008 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4401 stainless steel and the bottom bar is SAE-AISI 1008 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
93 to 100
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 40
22 to 33
Fatigue Strength, MPa 200 to 320
150 to 220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 410 to 550
220 to 230
Tensile Strength: Ultimate (UTS), MPa 600 to 900
330 to 370
Tensile Strength: Yield (Proof), MPa 230 to 570
190 to 310

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 950
400
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1400
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
62
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.8
1.4
Embodied Energy, MJ/kg 52
18
Embodied Water, L/kg 150
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
78 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 800
92 to 260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 32
12 to 13
Strength to Weight: Bending, points 20 to 26
13 to 15
Thermal Diffusivity, mm2/s 4.0
17
Thermal Shock Resistance, points 13 to 20
10 to 12

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.1
Chromium (Cr), % 16.5 to 18.5
0
Iron (Fe), % 62.8 to 71.5
99.31 to 99.7
Manganese (Mn), % 0 to 2.0
0.3 to 0.5
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 10 to 13
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.050