EN 1.4410 Stainless Steel vs. AISI 204 Stainless Steel

Both EN 1.4410 stainless steel and AISI 204 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is AISI 204 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
210 to 330
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 24
23 to 39
Fatigue Strength, MPa 410
320 to 720
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
77
Shear Strength, MPa 540
500 to 700
Tensile Strength: Ultimate (UTS), MPa 850
730 to 1100
Tensile Strength: Yield (Proof), MPa 600
380 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
850
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
10
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.0
2.4
Embodied Energy, MJ/kg 56
35
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 42
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
240 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 880
360 to 2940
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
27 to 40
Strength to Weight: Bending, points 26
24 to 31
Thermal Diffusivity, mm2/s 4.0
4.1
Thermal Shock Resistance, points 23
16 to 24

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 24 to 26
15 to 17
Iron (Fe), % 58.1 to 66.8
69.6 to 76.4
Manganese (Mn), % 0 to 2.0
7.0 to 9.0
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
1.5 to 3.0
Nitrogen (N), % 0.24 to 0.35
0.15 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030