EN 1.4410 Stainless Steel vs. ASTM A283 Carbon Steel

Both EN 1.4410 stainless steel and ASTM A283 carbon steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is ASTM A283 carbon steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
26 to 34
Fatigue Strength, MPa 410
150 to 190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
240 to 310
Tensile Strength: Ultimate (UTS), MPa 850
360 to 480
Tensile Strength: Yield (Proof), MPa 600
180 to 260

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51 to 53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 20
1.8
Density, g/cm3 7.8
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 56
18
Embodied Water, L/kg 180
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
100 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 880
91 to 180
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
13 to 17
Strength to Weight: Bending, points 26
14 to 17
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 23
11 to 15