EN 1.4410 Stainless Steel vs. ASTM A285 Carbon Steel

Both EN 1.4410 stainless steel and ASTM A285 carbon steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is ASTM A285 carbon steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
110 to 130
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
30 to 34
Fatigue Strength, MPa 410
150 to 180
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
250 to 290
Tensile Strength: Ultimate (UTS), MPa 850
380 to 450
Tensile Strength: Yield (Proof), MPa 600
190 to 230

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1400
1420 to 1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 56
18
Embodied Water, L/kg 180
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 880
94 to 150
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
13 to 16
Strength to Weight: Bending, points 26
15 to 17
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 23
12 to 14