Both EN 1.4410 stainless steel and AWS ER80S-B3L are iron alloys. They have 67% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is AWS ER80S-B3L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
19
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
74
Tensile Strength: Ultimate (UTS), MPa 850
630
Tensile Strength: Yield (Proof), MPa 600
530

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
4.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.8
Embodied Energy, MJ/kg 56
23
Embodied Water, L/kg 180
60

Common Calculations

PREN (Pitting Resistance) 42
6.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
120
Resilience: Unit (Modulus of Resilience), kJ/m3 880
730
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
22
Strength to Weight: Bending, points 26
21
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 23
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 24 to 26
2.3 to 2.7
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 58.1 to 66.8
93.6 to 96
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 3.0 to 4.5
0.9 to 1.2
Nickel (Ni), % 6.0 to 8.0
0 to 0.2
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0.4 to 0.7
Sulfur (S), % 0 to 0.015
0 to 0.025
Residuals, % 0
0 to 0.5