EN 1.4410 Stainless Steel vs. EN 1.0411 Steel

Both EN 1.4410 stainless steel and EN 1.0411 steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.0411 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
120 to 170
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
12 to 26
Fatigue Strength, MPa 410
200 to 320
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
300 to 350
Tensile Strength: Ultimate (UTS), MPa 850
420 to 570
Tensile Strength: Yield (Proof), MPa 600
270 to 480

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 56
18
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
43 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 880
190 to 610
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
15 to 20
Strength to Weight: Bending, points 26
16 to 20
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 23
13 to 18

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.030
0.18 to 0.22
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 58.1 to 66.8
98.7 to 99.1
Manganese (Mn), % 0 to 2.0
0.7 to 0.9
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.015
0 to 0.025