EN 1.4410 Stainless Steel vs. EN 1.3963 Alloy

Both EN 1.4410 stainless steel and EN 1.3963 alloy are iron alloys. They have 71% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.3963 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
29
Poisson's Ratio 0.27
0.3
Shear Modulus, GPa 81
72
Shear Strength, MPa 540
290
Tensile Strength: Ultimate (UTS), MPa 850
440
Tensile Strength: Yield (Proof), MPa 600
310

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Expansion, µm/m-K 13
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
25
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 4.0
4.8
Embodied Energy, MJ/kg 56
66
Embodied Water, L/kg 180
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 880
260
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 30
15
Strength to Weight: Bending, points 26
16
Thermal Shock Resistance, points 23
110

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 24 to 26
0 to 0.25
Iron (Fe), % 58.1 to 66.8
60.5 to 64.9
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 3.0 to 4.5
0 to 1.0
Nickel (Ni), % 6.0 to 8.0
35 to 37
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0.1 to 0.2