EN 1.4410 Stainless Steel vs. EN 1.4411 Stainless Steel

Both EN 1.4410 stainless steel and EN 1.4411 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.4411 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 24
17
Fatigue Strength, MPa 410
370
Impact Strength: V-Notched Charpy, J 90
68
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
78
Tensile Strength: Ultimate (UTS), MPa 850
870
Tensile Strength: Yield (Proof), MPa 600
600

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
880
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
3.0
Embodied Energy, MJ/kg 56
41
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 42
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
130
Resilience: Unit (Modulus of Resilience), kJ/m3 880
920
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
31
Strength to Weight: Bending, points 26
26
Thermal Diffusivity, mm2/s 4.0
4.6
Thermal Shock Resistance, points 23
28

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.060
Chromium (Cr), % 24 to 26
15 to 17
Iron (Fe), % 58.1 to 66.8
73.1 to 79.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.5
1.5 to 2.0
Nickel (Ni), % 6.0 to 8.0
4.0 to 6.0
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.025