EN 1.4410 Stainless Steel vs. EN 1.4911 Stainless Steel

Both EN 1.4410 stainless steel and EN 1.4911 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.4911 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 24
11
Fatigue Strength, MPa 410
530
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
76
Shear Strength, MPa 540
640
Tensile Strength: Ultimate (UTS), MPa 850
1070
Tensile Strength: Yield (Proof), MPa 600
970

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
430
Maximum Temperature: Mechanical, °C 1100
700
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
20
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
3.4
Embodied Energy, MJ/kg 56
49
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 42
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
120
Resilience: Unit (Modulus of Resilience), kJ/m3 880
2410
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
38
Strength to Weight: Bending, points 26
30
Thermal Diffusivity, mm2/s 4.0
5.4
Thermal Shock Resistance, points 23
37

Alloy Composition

Boron (B), % 0
0.0050 to 0.015
Carbon (C), % 0 to 0.030
0.050 to 0.12
Chromium (Cr), % 24 to 26
9.8 to 11.2
Cobalt (Co), % 0
5.0 to 7.0
Iron (Fe), % 58.1 to 66.8
75.7 to 83.8
Manganese (Mn), % 0 to 2.0
0.3 to 1.3
Molybdenum (Mo), % 3.0 to 4.5
0.5 to 1.0
Nickel (Ni), % 6.0 to 8.0
0.2 to 1.2
Niobium (Nb), % 0
0.2 to 0.5
Nitrogen (N), % 0.24 to 0.35
0 to 0.035
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0.1 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.015
Tungsten (W), % 0
0 to 0.7
Vanadium (V), % 0
0.1 to 0.4