EN 1.4410 Stainless Steel vs. EN 1.6781 Steel

Both EN 1.4410 stainless steel and EN 1.6781 steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.6781 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
250
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
17
Fatigue Strength, MPa 410
450
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 850
830
Tensile Strength: Yield (Proof), MPa 600
680

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
450
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 20
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.9
Embodied Energy, MJ/kg 56
25
Embodied Water, L/kg 180
60

Common Calculations

PREN (Pitting Resistance) 42
3.3
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
130
Resilience: Unit (Modulus of Resilience), kJ/m3 880
1220
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
29
Strength to Weight: Bending, points 26
25
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 23
24

Alloy Composition

Carbon (C), % 0 to 0.030
0.15 to 0.19
Chromium (Cr), % 24 to 26
1.3 to 1.8
Iron (Fe), % 58.1 to 66.8
92.6 to 94.6
Manganese (Mn), % 0 to 2.0
0.55 to 0.8
Molybdenum (Mo), % 3.0 to 4.5
0.45 to 0.6
Nickel (Ni), % 6.0 to 8.0
3.0 to 3.5
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.015