EN 1.4410 Stainless Steel vs. EN 1.8895 Steel

Both EN 1.4410 stainless steel and EN 1.8895 steel are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.8895 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
120
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
26
Fatigue Strength, MPa 410
220
Impact Strength: V-Notched Charpy, J 90
46
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
260
Tensile Strength: Ultimate (UTS), MPa 850
400
Tensile Strength: Yield (Proof), MPa 600
300

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.6
Embodied Energy, MJ/kg 56
21
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
96
Resilience: Unit (Modulus of Resilience), kJ/m3 880
240
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
14
Strength to Weight: Bending, points 26
15
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 23
12

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.030
0 to 0.13
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 58.1 to 66.8
97 to 99.98
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 3.0 to 4.5
0 to 0.2
Nickel (Ni), % 6.0 to 8.0
0 to 0.3
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.24 to 0.35
0 to 0.020
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.080