EN 1.4410 Stainless Steel vs. EN 1.8932 Steel

Both EN 1.4410 stainless steel and EN 1.8932 steel are iron alloys. They have 65% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.8932 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
20
Fatigue Strength, MPa 410
250
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
370
Tensile Strength: Ultimate (UTS), MPa 850
600
Tensile Strength: Yield (Proof), MPa 600
370

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.7
Embodied Energy, MJ/kg 56
24
Embodied Water, L/kg 180
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
100
Resilience: Unit (Modulus of Resilience), kJ/m3 880
370
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
21
Strength to Weight: Bending, points 26
20
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 23
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 24 to 26
0 to 0.3
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 58.1 to 66.8
95.5 to 98.9
Manganese (Mn), % 0 to 2.0
1.0 to 1.7
Molybdenum (Mo), % 3.0 to 4.5
0 to 0.1
Nickel (Ni), % 6.0 to 8.0
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.24 to 0.35
0 to 0.020
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0.1 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.015
Vanadium (V), % 0
0 to 0.2