EN 1.4410 Stainless Steel vs. EN 1.8958 Steel

Both EN 1.4410 stainless steel and EN 1.8958 steel are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.8958 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
130
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
19
Fatigue Strength, MPa 410
150
Impact Strength: V-Notched Charpy, J 90
30
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 540
270
Tensile Strength: Ultimate (UTS), MPa 850
430
Tensile Strength: Yield (Proof), MPa 600
220

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.5
Embodied Energy, MJ/kg 56
19
Embodied Water, L/kg 180
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
70
Resilience: Unit (Modulus of Resilience), kJ/m3 880
130
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
15
Strength to Weight: Bending, points 26
16
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 23
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.16
Chromium (Cr), % 24 to 26
0.35 to 0.85
Copper (Cu), % 0
0.2 to 0.6
Iron (Fe), % 58.1 to 66.8
96.5 to 99.3
Manganese (Mn), % 0 to 2.0
0.15 to 0.7
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
0 to 0.7
Nitrogen (N), % 0.24 to 0.35
0 to 0.010
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.45
Sulfur (S), % 0 to 0.015
0 to 0.040