EN 1.4410 Stainless Steel vs. SAE-AISI 12L14 Steel

Both EN 1.4410 stainless steel and SAE-AISI 12L14 steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is SAE-AISI 12L14 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
11 to 25
Fatigue Strength, MPa 410
190 to 290
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
72
Shear Strength, MPa 540
280 to 370
Tensile Strength: Ultimate (UTS), MPa 850
440 to 620
Tensile Strength: Yield (Proof), MPa 600
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 56
18
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
64 to 93
Resilience: Unit (Modulus of Resilience), kJ/m3 880
180 to 560
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
15 to 22
Strength to Weight: Bending, points 26
16 to 20
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 23
14 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 58.1 to 66.8
97.9 to 98.7
Lead (Pb), % 0
0.15 to 0.35
Manganese (Mn), % 0 to 2.0
0.85 to 1.2
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0.040 to 0.090
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0.26 to 0.35