EN 1.4410 Stainless Steel vs. Titanium 4-4-2

EN 1.4410 stainless steel belongs to the iron alloys classification, while titanium 4-4-2 belongs to the titanium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is titanium 4-4-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
110
Elongation at Break, % 24
10
Fatigue Strength, MPa 410
590 to 620
Poisson's Ratio 0.27
0.32
Shear Modulus, GPa 81
42
Shear Strength, MPa 540
690 to 750
Tensile Strength: Ultimate (UTS), MPa 850
1150 to 1250
Tensile Strength: Yield (Proof), MPa 600
1030 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 300
410
Maximum Temperature: Mechanical, °C 1100
310
Melting Completion (Liquidus), °C 1450
1610
Melting Onset (Solidus), °C 1400
1560
Specific Heat Capacity, J/kg-K 480
540
Thermal Conductivity, W/m-K 15
6.7
Thermal Expansion, µm/m-K 13
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
39
Density, g/cm3 7.8
4.7
Embodied Carbon, kg CO2/kg material 4.0
30
Embodied Energy, MJ/kg 56
480
Embodied Water, L/kg 180
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 880
4700 to 5160
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
34
Strength to Weight: Axial, points 30
68 to 74
Strength to Weight: Bending, points 26
52 to 55
Thermal Diffusivity, mm2/s 4.0
2.6
Thermal Shock Resistance, points 23
86 to 93

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
3.0 to 5.0
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 24 to 26
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 58.1 to 66.8
0 to 0.2
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 3.0 to 4.5
3.0 to 5.0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.24 to 0.35
0 to 0.050
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0.3 to 0.7
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
1.5 to 2.5
Titanium (Ti), % 0
85.8 to 92.2
Residuals, % 0
0 to 0.4