EN 1.4411 Stainless Steel vs. ASTM A204 Steel

Both EN 1.4411 stainless steel and ASTM A204 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4411 stainless steel and the bottom bar is ASTM A204 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
18 to 22
Fatigue Strength, MPa 370
200 to 220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 870
520 to 590
Tensile Strength: Yield (Proof), MPa 600
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 880
410
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1420 to 1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
52
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 41
20
Embodied Water, L/kg 130
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
90 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 920
220 to 290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31
18 to 21
Strength to Weight: Bending, points 26
18 to 20
Thermal Diffusivity, mm2/s 4.6
14
Thermal Shock Resistance, points 28
15 to 17