Both EN 1.4411 stainless steel and AWS ER90S-B9 are iron alloys. They have 88% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4411 stainless steel and the bottom bar is AWS ER90S-B9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
18
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 870
690
Tensile Strength: Yield (Proof), MPa 600
470

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
25
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 13
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 41
37
Embodied Water, L/kg 130
91

Common Calculations

PREN (Pitting Resistance) 22
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
110
Resilience: Unit (Modulus of Resilience), kJ/m3 920
570
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31
25
Strength to Weight: Bending, points 26
22
Thermal Diffusivity, mm2/s 4.6
6.9
Thermal Shock Resistance, points 28
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.060
0.070 to 0.13
Chromium (Cr), % 15 to 17
8.0 to 10.5
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 73.1 to 79.5
84.4 to 90.7
Manganese (Mn), % 0 to 1.0
0 to 1.2
Molybdenum (Mo), % 1.5 to 2.0
0.85 to 1.2
Nickel (Ni), % 4.0 to 6.0
0 to 0.8
Niobium (Nb), % 0
0.020 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0 to 0.8
0.15 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Vanadium (V), % 0
0.15 to 0.3
Residuals, % 0
0 to 0.5