EN 1.4411 Stainless Steel vs. S32205 Stainless Steel

Both EN 1.4411 stainless steel and S32205 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4411 stainless steel and the bottom bar is S32205 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
28
Fatigue Strength, MPa 370
370
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 870
740
Tensile Strength: Yield (Proof), MPa 600
510

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
440
Maximum Temperature: Mechanical, °C 880
1070
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
3.7
Embodied Energy, MJ/kg 41
50
Embodied Water, L/kg 130
160

Common Calculations

PREN (Pitting Resistance) 22
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
190
Resilience: Unit (Modulus of Resilience), kJ/m3 920
630
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31
26
Strength to Weight: Bending, points 26
23
Thermal Diffusivity, mm2/s 4.6
4.0
Thermal Shock Resistance, points 28
20

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.030
Chromium (Cr), % 15 to 17
22 to 23
Iron (Fe), % 73.1 to 79.5
63.7 to 70.4
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 1.5 to 2.0
3.0 to 3.5
Nickel (Ni), % 4.0 to 6.0
4.5 to 6.5
Nitrogen (N), % 0
0.14 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.020