EN 1.4417 Stainless Steel vs. EN 1.0591 Cast Steel
Both EN 1.4417 stainless steel and EN 1.0591 cast steel are iron alloys. They have 62% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.4417 stainless steel and the bottom bar is EN 1.0591 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Elongation at Break, % | 25 | |
19 |
Fatigue Strength, MPa | 380 | |
240 |
Impact Strength: V-Notched Charpy, J | 56 | |
29 |
Poisson's Ratio | 0.27 | |
0.29 |
Shear Modulus, GPa | 81 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 730 | |
620 |
Tensile Strength: Yield (Proof), MPa | 550 | |
360 |
Thermal Properties
Latent Heat of Fusion, J/g | 300 | |
250 |
Maximum Temperature: Mechanical, °C | 1100 | |
400 |
Melting Completion (Liquidus), °C | 1450 | |
1470 |
Melting Onset (Solidus), °C | 1410 | |
1430 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 17 | |
53 |
Thermal Expansion, µm/m-K | 13 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.8 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
8.9 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 21 | |
1.7 |
Density, g/cm3 | 7.9 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 4.1 | |
1.4 |
Embodied Energy, MJ/kg | 57 | |
18 |
Embodied Water, L/kg | 180 | |
45 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 730 | |
340 |
Stiffness to Weight: Axial, points | 15 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 26 | |
22 |
Strength to Weight: Bending, points | 23 | |
20 |
Thermal Diffusivity, mm2/s | 4.6 | |
14 |
Thermal Shock Resistance, points | 20 | |
20 |
Alloy Composition
Carbon (C), % | 0 to 0.030 | |
0 |
Chromium (Cr), % | 24 to 26 | |
0 |
Copper (Cu), % | 0 to 1.0 | |
0 |
Iron (Fe), % | 56.7 to 66.9 | |
99.935 to 100 |
Manganese (Mn), % | 0 to 1.5 | |
0 |
Molybdenum (Mo), % | 3.0 to 4.0 | |
0 |
Nickel (Ni), % | 6.0 to 8.5 | |
0 |
Nitrogen (N), % | 0.15 to 0.25 | |
0 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.035 |
Silicon (Si), % | 0 to 1.0 | |
0 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.030 |
Tungsten (W), % | 0 to 1.0 | |
0 |