EN 1.4418 Stainless Steel vs. R30816 Cobalt
EN 1.4418 stainless steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. They have a modest 26% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.4418 stainless steel and the bottom bar is R30816 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 16 to 20 | |
| 23 |
| Fatigue Strength, MPa | 350 to 480 | |
| 250 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 77 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 860 to 1000 | |
| 1020 |
| Tensile Strength: Yield (Proof), MPa | 540 to 790 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1540 |
| Melting Onset (Solidus), °C | 1400 | |
| 1460 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 420 |
| Thermal Conductivity, W/m-K | 15 | |
| 13 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 20 |
| Embodied Energy, MJ/kg | 39 | |
| 320 |
| Embodied Water, L/kg | 130 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 730 to 1590 | |
| 510 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 31 to 36 | |
| 31 |
| Strength to Weight: Bending, points | 26 to 28 | |
| 25 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 3.3 |
| Thermal Shock Resistance, points | 31 to 36 | |
| 28 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0.32 to 0.42 |
| Chromium (Cr), % | 15 to 17 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 40 to 49.8 |
| Iron (Fe), % | 73.2 to 80.2 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0 to 1.5 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0.8 to 1.5 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 3.5 to 4.5 |
| Tungsten (W), % | 0 | |
| 3.5 to 4.5 |