EN 1.4443 Stainless Steel vs. AISI 409 Stainless Steel

Both EN 1.4443 stainless steel and AISI 409 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4443 stainless steel and the bottom bar is AISI 409 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
24
Fatigue Strength, MPa 170
140
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 490
420
Tensile Strength: Yield (Proof), MPa 210
200

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 420
450
Maximum Temperature: Mechanical, °C 1000
710
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
6.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
2.0
Embodied Energy, MJ/kg 54
28
Embodied Water, L/kg 160
94

Common Calculations

PREN (Pitting Resistance) 28
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
83
Resilience: Unit (Modulus of Resilience), kJ/m3 110
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 3.9
6.7
Thermal Shock Resistance, points 11
15

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.080
Chromium (Cr), % 18 to 20
10.5 to 11.7
Iron (Fe), % 60.4 to 69.5
84.9 to 89.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.0
0
Nickel (Ni), % 10 to 13
0 to 0.5
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0 to 0.75