EN 1.4451 Stainless Steel vs. AISI 431 Stainless Steel

Both EN 1.4451 stainless steel and AISI 431 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is AISI 431 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
250
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
15 to 17
Fatigue Strength, MPa 370
430 to 610
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 750
890 to 1380
Tensile Strength: Yield (Proof), MPa 540
710 to 1040

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
400
Maximum Temperature: Mechanical, °C 1100
850
Melting Completion (Liquidus), °C 1430
1510
Melting Onset (Solidus), °C 1380
1450
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
26
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.8
2.2
Embodied Energy, MJ/kg 53
31
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 39
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
140 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 710
1270 to 2770
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
32 to 50
Strength to Weight: Bending, points 23
27 to 36
Thermal Diffusivity, mm2/s 4.5
7.0
Thermal Shock Resistance, points 16
28 to 43

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 25 to 27
15 to 17
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
78.2 to 83.8
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 5.0 to 7.0
1.3 to 2.5
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030