EN 1.4451 Stainless Steel vs. ASTM A182 Grade F92

Both EN 1.4451 stainless steel and ASTM A182 grade F92 are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is ASTM A182 grade F92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
240
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
22
Fatigue Strength, MPa 370
360
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 750
690
Tensile Strength: Yield (Proof), MPa 540
500

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
590
Melting Completion (Liquidus), °C 1430
1490
Melting Onset (Solidus), °C 1380
1450
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
26
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
10

Otherwise Unclassified Properties

Base Metal Price, % relative 20
11
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.8
2.8
Embodied Energy, MJ/kg 53
40
Embodied Water, L/kg 190
89

Common Calculations

PREN (Pitting Resistance) 39
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
140
Resilience: Unit (Modulus of Resilience), kJ/m3 710
650
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
24
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 4.5
6.9
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0 to 0.030
0.070 to 0.13
Chromium (Cr), % 25 to 27
8.5 to 9.5
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
85.8 to 89.1
Manganese (Mn), % 0 to 1.5
0.3 to 0.6
Molybdenum (Mo), % 2.5 to 3.5
0.3 to 0.6
Nickel (Ni), % 5.0 to 7.0
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0.12 to 0.22
0.030 to 0.070
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010