EN 1.4451 Stainless Steel vs. ASTM A204 Steel

Both EN 1.4451 stainless steel and ASTM A204 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is ASTM A204 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
18 to 22
Fatigue Strength, MPa 370
200 to 220
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 750
520 to 590
Tensile Strength: Yield (Proof), MPa 540
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1380
1420 to 1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
52
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.8
1.5
Embodied Energy, MJ/kg 53
20
Embodied Water, L/kg 190
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
90 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 710
220 to 290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
18 to 21
Strength to Weight: Bending, points 23
18 to 20
Thermal Diffusivity, mm2/s 4.5
14
Thermal Shock Resistance, points 16
15 to 17