EN 1.4451 Stainless Steel vs. AWS E309Nb

Both EN 1.4451 stainless steel and AWS E309Nb are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is AWS E309Nb.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
34
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 750
620

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
4.4
Embodied Energy, MJ/kg 53
64
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 39
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
22
Strength to Weight: Bending, points 23
21
Thermal Diffusivity, mm2/s 4.5
4.0
Thermal Shock Resistance, points 16
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.12
Chromium (Cr), % 25 to 27
22 to 25
Copper (Cu), % 2.8 to 3.5
0 to 0.75
Iron (Fe), % 56.2 to 64.6
54.8 to 64.8
Manganese (Mn), % 0 to 1.5
0.5 to 2.5
Molybdenum (Mo), % 2.5 to 3.5
0 to 0.75
Nickel (Ni), % 5.0 to 7.0
12 to 14
Niobium (Nb), % 0
0.7 to 1.0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030