MakeItFrom.com
Menu (ESC)

EN 1.4451 Stainless Steel vs. AWS ER100S-1

Both EN 1.4451 stainless steel and AWS ER100S-1 are iron alloys. They have 64% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is AWS ER100S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
18
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 750
770
Tensile Strength: Yield (Proof), MPa 540
700

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
49
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
3.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
1.8
Embodied Energy, MJ/kg 53
24
Embodied Water, L/kg 190
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
130
Resilience: Unit (Modulus of Resilience), kJ/m3 710
1290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
27
Strength to Weight: Bending, points 23
24
Thermal Diffusivity, mm2/s 4.5
13
Thermal Shock Resistance, points 16
23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 25 to 27
0 to 0.3
Copper (Cu), % 2.8 to 3.5
0 to 0.25
Iron (Fe), % 56.2 to 64.6
93.5 to 96.9
Manganese (Mn), % 0 to 1.5
1.3 to 1.8
Molybdenum (Mo), % 2.5 to 3.5
0.25 to 0.55
Nickel (Ni), % 5.0 to 7.0
1.4 to 2.1
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0 to 1.0
0.2 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0
0 to 0.050
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0
0 to 0.5