EN 1.4451 Stainless Steel vs. EN 1.4436 Stainless Steel

Both EN 1.4451 stainless steel and EN 1.4436 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 88% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is EN 1.4436 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
42
Fatigue Strength, MPa 370
220
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 750
620
Tensile Strength: Yield (Proof), MPa 540
240

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.8
3.9
Embodied Energy, MJ/kg 53
54
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 39
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
210
Resilience: Unit (Modulus of Resilience), kJ/m3 710
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
22
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 4.5
4.0
Thermal Shock Resistance, points 16
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 25 to 27
16.5 to 18.5
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
62.3 to 70.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 2.5 to 3.5
2.5 to 3.0
Nickel (Ni), % 5.0 to 7.0
10.5 to 13
Nitrogen (N), % 0.12 to 0.22
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015