EN 1.4451 Stainless Steel vs. EN 1.4986 Stainless Steel

Both EN 1.4451 stainless steel and EN 1.4986 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is EN 1.4986 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
230
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
18
Fatigue Strength, MPa 370
350
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 750
750
Tensile Strength: Yield (Proof), MPa 540
560

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 450
520
Maximum Temperature: Mechanical, °C 1100
940
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
25
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.8
4.8
Embodied Energy, MJ/kg 53
67
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 39
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
120
Resilience: Unit (Modulus of Resilience), kJ/m3 710
790
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
26
Strength to Weight: Bending, points 23
23
Thermal Diffusivity, mm2/s 4.5
4.0
Thermal Shock Resistance, points 16
16

Alloy Composition

Boron (B), % 0
0.050 to 0.1
Carbon (C), % 0 to 0.030
0.040 to 0.1
Chromium (Cr), % 25 to 27
15.5 to 17.5
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
59.4 to 66.6
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 2.5 to 3.5
1.6 to 2.0
Nickel (Ni), % 5.0 to 7.0
15.5 to 17.5
Niobium (Nb), % 0
0.4 to 1.2
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0.3 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030