EN 1.4451 Stainless Steel vs. EN 1.7779 Steel

Both EN 1.4451 stainless steel and EN 1.7779 steel are iron alloys. They have 65% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is EN 1.7779 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
240
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
16
Fatigue Strength, MPa 370
430
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 750
810
Tensile Strength: Yield (Proof), MPa 540
660

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
470
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
39
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
4.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
2.8
Embodied Energy, MJ/kg 53
41
Embodied Water, L/kg 190
64

Common Calculations

PREN (Pitting Resistance) 39
5.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
120
Resilience: Unit (Modulus of Resilience), kJ/m3 710
1150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
29
Strength to Weight: Bending, points 23
25
Thermal Diffusivity, mm2/s 4.5
11
Thermal Shock Resistance, points 16
23

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.030
0.17 to 0.23
Chromium (Cr), % 25 to 27
3.0 to 3.3
Copper (Cu), % 2.8 to 3.5
0 to 0.3
Iron (Fe), % 56.2 to 64.6
93.8 to 95.4
Manganese (Mn), % 0 to 1.5
0.3 to 0.5
Molybdenum (Mo), % 2.5 to 3.5
0.5 to 0.6
Nickel (Ni), % 5.0 to 7.0
0 to 0.3
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.010
Vanadium (V), % 0
0.45 to 0.55