EN 1.4451 Stainless Steel vs. Monel K-500

EN 1.4451 stainless steel belongs to the iron alloys classification, while Monel K-500 belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is Monel K-500.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
160
Elongation at Break, % 25
25 to 36
Fatigue Strength, MPa 370
260 to 560
Poisson's Ratio 0.27
0.32
Shear Modulus, GPa 80
61
Tensile Strength: Ultimate (UTS), MPa 750
640 to 1100
Tensile Strength: Yield (Proof), MPa 540
310 to 880

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1430
1350
Melting Onset (Solidus), °C 1380
1320
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 17
18
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
3.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
50
Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 3.8
8.1
Embodied Energy, MJ/kg 53
120
Embodied Water, L/kg 190
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
180 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 710
300 to 2420
Stiffness to Weight: Axial, points 14
10
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 27
21 to 35
Strength to Weight: Bending, points 23
19 to 27
Thermal Diffusivity, mm2/s 4.5
4.8
Thermal Shock Resistance, points 16
21 to 36

Alloy Composition

Aluminum (Al), % 0
2.3 to 3.2
Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 25 to 27
0
Copper (Cu), % 2.8 to 3.5
27 to 33
Iron (Fe), % 56.2 to 64.6
0 to 2.0
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 5.0 to 7.0
63 to 70.4
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0.35 to 0.85