EN 1.4451 Stainless Steel vs. N06025 Nickel

EN 1.4451 stainless steel belongs to the iron alloys classification, while N06025 nickel belongs to the nickel alloys. They have 41% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is N06025 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
32
Fatigue Strength, MPa 370
220
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 750
760
Tensile Strength: Yield (Proof), MPa 540
310

Thermal Properties

Latent Heat of Fusion, J/g 300
320
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1430
1350
Melting Onset (Solidus), °C 1380
1300
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
11
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
50
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 3.8
8.4
Embodied Energy, MJ/kg 53
120
Embodied Water, L/kg 190
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
190
Resilience: Unit (Modulus of Resilience), kJ/m3 710
240
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
26
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 4.5
2.9
Thermal Shock Resistance, points 16
21

Alloy Composition

Aluminum (Al), % 0
1.8 to 2.4
Carbon (C), % 0 to 0.030
0.15 to 0.25
Chromium (Cr), % 25 to 27
24 to 26
Copper (Cu), % 2.8 to 3.5
0 to 0.1
Iron (Fe), % 56.2 to 64.6
8.0 to 11
Manganese (Mn), % 0 to 1.5
0 to 0.15
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 5.0 to 7.0
59.2 to 65.9
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0.1 to 0.2
Yttrium (Y), % 0
0.050 to 0.12
Zinc (Zn), % 0
0.010 to 0.1