EN 1.4451 Stainless Steel vs. N08535 Stainless Steel

Both EN 1.4451 stainless steel and N08535 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is N08535 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
46
Fatigue Strength, MPa 370
220
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 750
570
Tensile Strength: Yield (Proof), MPa 540
240

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
13
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.8
6.3
Embodied Energy, MJ/kg 53
87
Embodied Water, L/kg 190
230

Common Calculations

PREN (Pitting Resistance) 39
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
210
Resilience: Unit (Modulus of Resilience), kJ/m3 710
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
20
Strength to Weight: Bending, points 23
19
Thermal Diffusivity, mm2/s 4.5
3.3
Thermal Shock Resistance, points 16
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 25 to 27
24 to 27
Copper (Cu), % 2.8 to 3.5
0 to 1.5
Iron (Fe), % 56.2 to 64.6
29.4 to 44.5
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
2.5 to 4.0
Nickel (Ni), % 5.0 to 7.0
29 to 36.5
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030