EN 1.4451 Stainless Steel vs. S32050 Stainless Steel

Both EN 1.4451 stainless steel and S32050 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is S32050 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
220
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 25
46
Fatigue Strength, MPa 370
340
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
81
Tensile Strength: Ultimate (UTS), MPa 750
770
Tensile Strength: Yield (Proof), MPa 540
370

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
440
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
12
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 20
31
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.8
6.0
Embodied Energy, MJ/kg 53
81
Embodied Water, L/kg 190
210

Common Calculations

PREN (Pitting Resistance) 39
48
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
290
Resilience: Unit (Modulus of Resilience), kJ/m3 710
330
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
27
Strength to Weight: Bending, points 23
23
Thermal Diffusivity, mm2/s 4.5
3.3
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 25 to 27
22 to 24
Copper (Cu), % 2.8 to 3.5
0 to 0.4
Iron (Fe), % 56.2 to 64.6
43.1 to 51.8
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 2.5 to 3.5
6.0 to 6.6
Nickel (Ni), % 5.0 to 7.0
20 to 23
Nitrogen (N), % 0.12 to 0.22
0.21 to 0.32
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.020