EN 1.4451 Stainless Steel vs. S32053 Stainless Steel

Both EN 1.4451 stainless steel and S32053 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is S32053 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 25
46
Fatigue Strength, MPa 370
310
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 750
730
Tensile Strength: Yield (Proof), MPa 540
330

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
440
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
13
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.8
6.1
Embodied Energy, MJ/kg 53
83
Embodied Water, L/kg 190
210

Common Calculations

PREN (Pitting Resistance) 39
44
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
270
Resilience: Unit (Modulus of Resilience), kJ/m3 710
270
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
25
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 4.5
3.3
Thermal Shock Resistance, points 16
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 25 to 27
22 to 24
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
41.7 to 48.8
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
5.0 to 6.0
Nickel (Ni), % 5.0 to 7.0
24 to 26
Nitrogen (N), % 0.12 to 0.22
0.17 to 0.22
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.010