EN 1.4451 Stainless Steel vs. S35000 Stainless Steel

Both EN 1.4451 stainless steel and S35000 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
2.3 to 14
Fatigue Strength, MPa 370
380 to 520
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 750
1300 to 1570
Tensile Strength: Yield (Proof), MPa 540
660 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
16
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
14
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
3.2
Embodied Energy, MJ/kg 53
44
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 39
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
28 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 710
1070 to 3360
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
46 to 56
Strength to Weight: Bending, points 23
34 to 38
Thermal Diffusivity, mm2/s 4.5
4.4
Thermal Shock Resistance, points 16
42 to 51

Alloy Composition

Carbon (C), % 0 to 0.030
0.070 to 0.11
Chromium (Cr), % 25 to 27
16 to 17
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
72.7 to 76.9
Manganese (Mn), % 0 to 1.5
0.5 to 1.3
Molybdenum (Mo), % 2.5 to 3.5
2.5 to 3.2
Nickel (Ni), % 5.0 to 7.0
4.0 to 5.0
Nitrogen (N), % 0.12 to 0.22
0.070 to 0.13
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030