EN 1.4451 Stainless Steel vs. S36200 Stainless Steel

Both EN 1.4451 stainless steel and S36200 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is S36200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
3.4 to 4.6
Fatigue Strength, MPa 370
450 to 570
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 750
1180 to 1410
Tensile Strength: Yield (Proof), MPa 540
960 to 1240

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
530
Maximum Temperature: Mechanical, °C 1100
820
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
16
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
12
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
2.8
Embodied Energy, MJ/kg 53
40
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 39
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
46 to 51
Resilience: Unit (Modulus of Resilience), kJ/m3 710
2380 to 3930
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
42 to 50
Strength to Weight: Bending, points 23
32 to 36
Thermal Diffusivity, mm2/s 4.5
4.3
Thermal Shock Resistance, points 16
40 to 48

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 25 to 27
14 to 14.5
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
75.4 to 79.5
Manganese (Mn), % 0 to 1.5
0 to 0.5
Molybdenum (Mo), % 2.5 to 3.5
0 to 0.3
Nickel (Ni), % 5.0 to 7.0
6.5 to 7.0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0.6 to 0.9