EN 1.4451 Stainless Steel vs. S40975 Stainless Steel

Both EN 1.4451 stainless steel and S40975 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is S40975 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
22
Fatigue Strength, MPa 370
210
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 750
460
Tensile Strength: Yield (Proof), MPa 540
310

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
710
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
26
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
6.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
2.0
Embodied Energy, MJ/kg 53
28
Embodied Water, L/kg 190
95

Common Calculations

PREN (Pitting Resistance) 39
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
93
Resilience: Unit (Modulus of Resilience), kJ/m3 710
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
17
Strength to Weight: Bending, points 23
17
Thermal Diffusivity, mm2/s 4.5
7.0
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 25 to 27
10.5 to 11.7
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
84.4 to 89
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 5.0 to 7.0
0.5 to 1.0
Nitrogen (N), % 0.12 to 0.22
0 to 0.030
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0 to 0.75