EN 1.4458 Stainless Steel vs. 5050 Aluminum

EN 1.4458 stainless steel belongs to the iron alloys classification, while 5050 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is 5050 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
36 to 68
Elastic (Young's, Tensile) Modulus, GPa 200
68
Elongation at Break, % 34
1.7 to 22
Fatigue Strength, MPa 150
45 to 100
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 78
26
Tensile Strength: Ultimate (UTS), MPa 510
140 to 250
Tensile Strength: Yield (Proof), MPa 190
50 to 210

Thermal Properties

Latent Heat of Fusion, J/g 300
400
Maximum Temperature: Mechanical, °C 1100
180
Melting Completion (Liquidus), °C 1420
650
Melting Onset (Solidus), °C 1370
630
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 16
190
Thermal Expansion, µm/m-K 15
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
50
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
170

Otherwise Unclassified Properties

Base Metal Price, % relative 30
9.5
Density, g/cm3 8.0
2.7
Embodied Carbon, kg CO2/kg material 5.4
8.4
Embodied Energy, MJ/kg 75
150
Embodied Water, L/kg 200
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
4.1 to 24
Resilience: Unit (Modulus of Resilience), kJ/m3 89
18 to 330
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 17
15 to 26
Strength to Weight: Bending, points 18
22 to 33
Thermal Diffusivity, mm2/s 4.2
79
Thermal Shock Resistance, points 12
6.3 to 11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
96.3 to 98.9
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0 to 0.1
Copper (Cu), % 0 to 2.0
0 to 0.2
Iron (Fe), % 40.2 to 53
0 to 0.7
Magnesium (Mg), % 0
1.1 to 1.8
Manganese (Mn), % 0 to 2.0
0 to 0.1
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 26 to 30
0
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.025
0
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.15