EN 1.4458 Stainless Steel vs. ASTM Grade HF Steel

Both EN 1.4458 stainless steel and ASTM grade HF steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is ASTM grade HF steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
29
Fatigue Strength, MPa 150
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 510
550
Tensile Strength: Yield (Proof), MPa 190
270

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
16
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 30
17
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
3.2
Embodied Energy, MJ/kg 75
46
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 30
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
130
Resilience: Unit (Modulus of Resilience), kJ/m3 89
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.2
4.2
Thermal Shock Resistance, points 12
12

Alloy Composition

Carbon (C), % 0 to 0.030
0.2 to 0.4
Chromium (Cr), % 19 to 22
18 to 23
Copper (Cu), % 0 to 2.0
0
Iron (Fe), % 40.2 to 53
60 to 73.8
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 2.5
0 to 0.5
Nickel (Ni), % 26 to 30
8.0 to 12
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 2.0
Sulfur (S), % 0 to 0.025
0 to 0.040