EN 1.4458 Stainless Steel vs. AWS E80C-B3L

Both EN 1.4458 stainless steel and AWS E80C-B3L are iron alloys. They have 51% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is AWS E80C-B3L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 510
620
Tensile Strength: Yield (Proof), MPa 190
540

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
41
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 30
4.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 75
24
Embodied Water, L/kg 200
60

Common Calculations

PREN (Pitting Resistance) 30
5.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 89
760
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 19 to 22
2.0 to 2.5
Copper (Cu), % 0 to 2.0
0 to 0.35
Iron (Fe), % 40.2 to 53
93.5 to 96.5
Manganese (Mn), % 0 to 2.0
0.4 to 1.0
Molybdenum (Mo), % 2.0 to 2.5
0.9 to 1.2
Nickel (Ni), % 26 to 30
0 to 0.2
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0.25 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5