EN 1.4458 Stainless Steel vs. EN 1.0258 Steel

Both EN 1.4458 stainless steel and EN 1.0258 steel are iron alloys. They have 48% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is EN 1.0258 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
23
Fatigue Strength, MPa 150
200
Impact Strength: V-Notched Charpy, J 67
38
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 510
490
Tensile Strength: Yield (Proof), MPa 190
290

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.1
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
1.5
Embodied Energy, MJ/kg 75
19
Embodied Water, L/kg 200
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
95
Resilience: Unit (Modulus of Resilience), kJ/m3 89
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 4.2
13
Thermal Shock Resistance, points 12
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 19 to 22
0 to 0.3
Copper (Cu), % 0 to 2.0
0 to 0.3
Iron (Fe), % 40.2 to 53
96.9 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.4
Molybdenum (Mo), % 2.0 to 2.5
0 to 0.080
Nickel (Ni), % 26 to 30
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020