EN 1.4458 Stainless Steel vs. EN 1.7379 Steel

Both EN 1.4458 stainless steel and EN 1.7379 steel are iron alloys. They have 51% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is EN 1.7379 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
21
Fatigue Strength, MPa 150
320
Impact Strength: V-Notched Charpy, J 67
45
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Tensile Strength: Ultimate (UTS), MPa 510
670
Tensile Strength: Yield (Proof), MPa 190
460

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1100
460
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
39
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 30
3.8
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 75
23
Embodied Water, L/kg 200
59

Common Calculations

PREN (Pitting Resistance) 30
5.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120
Resilience: Unit (Modulus of Resilience), kJ/m3 89
550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12
19

Alloy Composition

Carbon (C), % 0 to 0.030
0.13 to 0.2
Chromium (Cr), % 19 to 22
2.0 to 2.5
Copper (Cu), % 0 to 2.0
0
Iron (Fe), % 40.2 to 53
94.5 to 96.5
Manganese (Mn), % 0 to 2.0
0.5 to 0.9
Molybdenum (Mo), % 2.0 to 2.5
0.9 to 1.2
Nickel (Ni), % 26 to 30
0
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030