EN 1.4458 Stainless Steel vs. EN 1.8874 Steel

Both EN 1.4458 stainless steel and EN 1.8874 steel are iron alloys. They have 50% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is EN 1.8874 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
19
Fatigue Strength, MPa 150
340
Impact Strength: V-Notched Charpy, J 67
68
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 510
660
Tensile Strength: Yield (Proof), MPa 190
500

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
39
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
3.2
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 75
24
Embodied Water, L/kg 200
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120
Resilience: Unit (Modulus of Resilience), kJ/m3 89
670
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 4.2
10
Thermal Shock Resistance, points 12
19

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 19 to 22
0 to 1.0
Copper (Cu), % 0 to 2.0
0 to 0.3
Iron (Fe), % 40.2 to 53
93.6 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.7
Molybdenum (Mo), % 2.0 to 2.5
0 to 0.7
Nickel (Ni), % 26 to 30
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0 to 0.2
0 to 0.015
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15