EN 1.4458 Stainless Steel vs. Grade TDCrV Steel

Both EN 1.4458 stainless steel and grade TDCrV steel are iron alloys. They have 48% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is grade TDCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
520
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 510
1730

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
49
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.1
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.9
Embodied Energy, MJ/kg 75
26
Embodied Water, L/kg 200
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
61
Strength to Weight: Bending, points 18
41
Thermal Diffusivity, mm2/s 4.2
13
Thermal Shock Resistance, points 12
51

Alloy Composition

Carbon (C), % 0 to 0.030
0.62 to 0.72
Chromium (Cr), % 19 to 22
0.4 to 0.6
Copper (Cu), % 0 to 2.0
0 to 0.1
Iron (Fe), % 40.2 to 53
97.8 to 98.8
Manganese (Mn), % 0 to 2.0
0.5 to 0.9
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 26 to 30
0
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.020
Vanadium (V), % 0
0.15 to 0.25