EN 1.4458 Stainless Steel vs. SAE-AISI A4 Steel

Both EN 1.4458 stainless steel and SAE-AISI A4 steel are iron alloys. They have 51% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is SAE-AISI A4 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 510
710 to 2050

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
40
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 30
3.9
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 75
24
Embodied Water, L/kg 200
59

Common Calculations

PREN (Pitting Resistance) 30
5.3
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
25 to 73
Strength to Weight: Bending, points 18
23 to 46
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12
23 to 67

Alloy Composition

Carbon (C), % 0 to 0.030
1.0 to 1.1
Chromium (Cr), % 19 to 22
0.9 to 2.2
Copper (Cu), % 0 to 2.0
0 to 0.25
Iron (Fe), % 40.2 to 53
92 to 95.5
Manganese (Mn), % 0 to 2.0
1.8 to 2.2
Molybdenum (Mo), % 2.0 to 2.5
0.9 to 1.4
Nickel (Ni), % 26 to 30
0 to 0.3
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030