EN 1.4458 Stainless Steel vs. N08535 Stainless Steel

Both EN 1.4458 stainless steel and N08535 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is N08535 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
46
Fatigue Strength, MPa 150
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 510
570
Tensile Strength: Yield (Proof), MPa 190
240

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 430
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
13
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
36
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 5.4
6.3
Embodied Energy, MJ/kg 75
87
Embodied Water, L/kg 200
230

Common Calculations

PREN (Pitting Resistance) 30
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
210
Resilience: Unit (Modulus of Resilience), kJ/m3 89
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.2
3.3
Thermal Shock Resistance, points 12
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 19 to 22
24 to 27
Copper (Cu), % 0 to 2.0
0 to 1.5
Iron (Fe), % 40.2 to 53
29.4 to 44.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.0 to 2.5
2.5 to 4.0
Nickel (Ni), % 26 to 30
29 to 36.5
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030