EN 1.4469 Stainless Steel vs. Automotive Grey Cast Iron

Both EN 1.4469 stainless steel and automotive grey cast iron are iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4469 stainless steel and the bottom bar is automotive grey cast iron.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
180
Elongation at Break, % 25
9.6 to 14
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
69 to 70
Tensile Strength: Ultimate (UTS), MPa 740
140 to 290
Tensile Strength: Yield (Proof), MPa 550
94 to 200

Thermal Properties

Latent Heat of Fusion, J/g 300
260 to 280
Melting Completion (Liquidus), °C 1450
1380 to 1390
Melting Onset (Solidus), °C 1400
1340 to 1350
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 17
41 to 43
Thermal Expansion, µm/m-K 13
12 to 14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4 to 7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.8 to 9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.9 to 3.0
Density, g/cm3 7.8
7.5 to 7.6
Embodied Carbon, kg CO2/kg material 4.1
1.5 to 1.7
Embodied Energy, MJ/kg 57
21 to 24
Embodied Water, L/kg 180
44 to 51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
18 to 25
Resilience: Unit (Modulus of Resilience), kJ/m3 730
25 to 110
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
5.2 to 11
Strength to Weight: Bending, points 23
8.0 to 13
Thermal Diffusivity, mm2/s 4.6
11 to 12
Thermal Shock Resistance, points 20
4.2 to 8.6