EN 1.4470 Stainless Steel vs. EN 1.4864 Stainless Steel

Both EN 1.4470 stainless steel and EN 1.4864 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4470 stainless steel and the bottom bar is EN 1.4864 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
33
Fatigue Strength, MPa 320
200
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 680
650
Tensile Strength: Yield (Proof), MPa 480
260

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1060
1100
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 18
13
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 17
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.6
5.3
Embodied Energy, MJ/kg 49
75
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 34
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
170
Resilience: Unit (Modulus of Resilience), kJ/m3 570
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
23
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 4.8
3.3
Thermal Shock Resistance, points 18
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 21 to 23
15 to 17
Iron (Fe), % 63.7 to 71.9
41.7 to 51
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 4.5 to 6.5
33 to 37
Nitrogen (N), % 0.12 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
1.0 to 2.0
Sulfur (S), % 0 to 0.025
0 to 0.015