EN 1.4477 Stainless Steel vs. AISI 440B Stainless Steel

Both EN 1.4477 stainless steel and AISI 440B stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4477 stainless steel and the bottom bar is AISI 440B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 22 to 23
3.0 to 18
Fatigue Strength, MPa 420 to 490
260 to 850
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
77
Shear Strength, MPa 550 to 580
460 to 1110
Tensile Strength: Ultimate (UTS), MPa 880 to 930
740 to 1930
Tensile Strength: Yield (Proof), MPa 620 to 730
430 to 1860

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 460
390
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1430
1480
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 13
23
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
9.0
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.7
2.2
Embodied Energy, MJ/kg 52
31
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 41
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180 to 190
57 to 110
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31 to 33
27 to 70
Strength to Weight: Bending, points 26 to 27
24 to 45
Thermal Diffusivity, mm2/s 3.5
6.1
Thermal Shock Resistance, points 23 to 25
27 to 70

Alloy Composition

Carbon (C), % 0 to 0.030
0.75 to 1.0
Chromium (Cr), % 28 to 30
16 to 18
Copper (Cu), % 0 to 0.8
0
Iron (Fe), % 56.6 to 63.6
78.2 to 83.3
Manganese (Mn), % 0.8 to 1.5
0 to 1.0
Molybdenum (Mo), % 1.5 to 2.6
0 to 0.75
Nickel (Ni), % 5.8 to 7.5
0
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015